The ceiling suspension system shall be exposed lay in system to fit 600 mm X 600 mm or 600 mm X 1200 mm ceiling modules. It shall be suspended to the shoffit by a 4mm diameter adjustable quick fit hanger rod system. Main tee shall be in 33 m height and exposed portion shall be 24 mm. Cross tee shall be 25mm height and exposed portion is 24mm.

All system components are made up of roll formed hot dipped galvanized steel of 0.30mm thickness with zinc coating of not less than 120g/m2 and a minimum tensile strength of 240 mpa. Wall angle are 24mm height X 24 mm expose portion made up of .4 mm thick pre coated coil.
Both ends of the main tee have integral spices which can be joined firmly be inserting a tab on the one end of the one section into slot in the adjoining section.

 The exposed flange finish shall be pre painted polyester coated galvanized still not less than .30 in off white color with coating thickness of 20 microns top coat and 8 microns primer alkyd backer on backside.

The main runner has fire notches to sustain grid system during fire.

                  

It is economical , easy to install, using less labour to complete installation in minimum time as compared with conventional extruded aluminum tee system.

Interchangeability of crass tee between systems, promote lower inventory requirement and greater field flexibility. The straight anti locking feature of the section allows the system to be installed easily within close proximity of the overheads.

The system promote complete design flexibility, and it is capable of sustaining loads normally designed into suspended tee system.

Overlap type of cross tee provide complete flush joint, eliminating joints between main runner and cross tees and rigidity at fixtures. In line cross tee provide true double lock action.

 

 

  • Steel material is processed by pre-painted hot dip galvanized.

  • Our zinc mass coating is 120 gm.m2 . Salt spray test for the white pre-painted cap is for 300 hours.

  • The material is processed with 20 micron polyester pre-painted.

  • The anti-Rusting process has been incorporated into the galvanized steel.

  • Tee bars are produced by fully-automatic machine controlling the production of straight material to maximum 0.1mm tolerance ensuring consistent dimensioning of the grid module after installation.

  • Load bearing capacity when the span is 1.2 meter, supported with hanger wire from roof for type 1 is 8.45 kg/m2 and type II is 12.05 kg/m2

                                            Specification